Hastelloy C22 (UNS N06022)se yon alyaj nikèl-chromium-molybdène-tengstèn. Nikèl C22 montre ekselan rezistans nan oksidasyon ak diminye anviwònman asid. Alloy C22 tou montre rezistans ekselan nan twou, korozyon fant, ak krak korozyon estrès. Materyèl 2.4062 la reziste fòmasyon fwontyè grenn jaden presipite nan zòn ki afekte chalè soude a, sa ki fè li apwopriye pou itilize nan kondisyon an tankou soude. HASTELLOY Alloy C22 se duktil, kidonk li se fasil frèt travay, ak frèt fòme se metòd la fòme pi pito.
Limit Konpozisyon Chimik
| % pwa | Ni | Kr | Mo | Fe | W | Co | V | C | Mn | S | Si | P |
| Alyaj 22 | Bal | 20-22 | 12.5-14.5 | 2-6 | 2.5-3.5 | 2.5 max | 0.35 max | 0.015 max | 0.50 max | 0.02 max | 0.08 max | 0.02 max |
DisponibEspesifikasyon
| Bar | ASTM B574, ASTM B462, DIN 17752, ISO 9724, ISO 9723 |
| Plak | ASTM B575 |
| Fèy | ASTM B575, ASTM B906, ASME SB 575 ASME SB 906, ASME Kòd Ka 2226, ISO 6208, DIN 17750 |
| Dezabiye | ASTM B575, ASTM B906, ASME SB 575 ASME SB 906, ASME Kòd Ka 2226, ISO 6208, DIN 17750 |
| Fòje | ASTM B564, ASTM SB564, DIN 17754 |
| Tiyo | Tiyo san pwoblèm ASTM B622, soude tiyo ASTM B619, ASTM B775 |
| Tib | Tib san pwoblèm, ASTM B622, ASTM B829, Weld Tib ASTM B626, DIN 17751, ISO 6207 |
| BW Fitting | ASTM B366, ASME SB366 |
Aplikasyon Alloy C22 UNS N06022
Klorasyon marinated, plant sulfonasyon, kontwòl polisyon, echanjeur chalè tubulaires, pwosesis chimik, marin, ak repwosesaj gaz nikleyè.
Pwopriyete Tensile nan solisyon chalè treteFèy Hastelloy C22:
20 degre:
- Sede fòs: 407 MPa
- Fòs rupture: 800 MPa
- elongasyon: 57%
Pwopriyete fizik tanperati chanm yo:
- Dansite: 8.7 g/cm3
- Tanperati fonn: 1357-1400 degre
Koefisyan ekspansyon tèmik tanperati ki wo, soti nan 20 degre:
- 100 degre: 12.4 μm/m⋅K
- 300 degre: 12.6 μm/m⋅K
- 400 degre: 13.1 μm/m⋅K
- 500 degre: 13.7 μm/m⋅K
- 600 degre: 14.3 μm/m⋅K
- 700 degre: 14.9 μm/m⋅K
- 800 degre: 15.5 μm/m⋅K
- 900 degre: 15.9 μm/m⋅K
Nikèl Alloy C22 Tretman Chalè
- Fòje: 1232-954 degre
- Tretman solisyon: 1120±14 degre, 30 minit, WQ