Fèy Hastelloy C276
1. estanda: ASTM B575, ASTM B333, ASTM B906
2. Lajè: 0 ~ 2500mm oswa Customized
3. Longè: 0 ~ 12m oswa Customized
4. epesè: 0.3 ~ 20mm oswa Customized
5. Klas: Hastelloy c276, UNS N10276, EN 2.4819
Hastelloy c276 fèygen gwo rezistans nan klori estrès korozyon krak, pitting, korozyon fant ak korozyon jeneral. Paske nan adisyon a nan molibdèn segondè ak kontni CHROMIUM ak tengstèn. alyaj nikèl C-276 epesè fèy varye ant 3/16 pous (4.8 mm) ak 2 ½ pous (63.5 mm). Li ka opere nan atmosfè oksidan jiska 1900oF (1038 degre). Li se youn nan premye materyèl ki reziste korozyon nan aplikasyon endistriyèl.
Aplikasyon pouHastelloy C-276 Fèy:
- Plant chimik
- Petrochimik
- Desulfurization gaz lafimen
- Endistri kaka ak papye
- Pwoteksyon anviwònman an
- Echanjeur chalè
- Ekipman desulfurization gaz lafimen
- Ponp likid korozyon reziste
Hastelloy c-276 fèy analiz chimik
| Nikèl | Balans | Manganèz | 1 |
| Molybdène | 15.0 min.-17.{3}} max. | Kabòn | 0.01 |
| Kwòm | 14.5 min.-16.5 max. | Vanadyòm | 0.35 |
| Fè | 4.0 min.-7.{3}} max. | Fosfò | 0.04 |
| Tengstèn | 3.0 min.-4.5 max. | Souf | 0.03 |
| Cobalt | 2.5 | Silisyòm | 0.08 |
Pwopriyete mekanik nan alyaj C276
| Pwopriyete | Metrik | Imperial |
| Fòs rupture (@epesè 4.80-25.4 mm, 538 degre /@epesè 0.189-1.00 nan, 1000 degre F) | 601.2 MPa | 87200 psi |
| Fòs sede ({{0}}.2% konpanse, @epesè 2.40 mm, 427 degre /@epesè 0.0945 pous, 801 degre F) | 204.8 MPa | 29700 psi |
| Modil elastik (RT) | 205 GPa | 29700 ksi |
| Elongasyon nan kase (nan 50.8 mm, @epesè 1.60-4.70 mm, 204 degre /@epesè 0.0630-0.185 nan, 399 degre F) | 56% | 56% |
| Dite, Rockwell B (plak) | 87 | 87 |
Hastelloy C276 Mwayèn Tensile Done
| Fòm | Kondisyon | Tès | Ultim | Sede | Elongasyon |
| Tanperati, | tansyon | Fòs nan | nan 2" pousan | ||
| degre F (degre) | Fòs | 0.2% konpanse | |||
| ksi (MPa) | ksi (MPa) | ||||
| Fèy, 0.063 to 0.187" Epè |
Chalè trete nan | 400 (204) | 100.8 (695) | 42.1 (290) | 56 |
| 2050 degre F | 600 (316) | 97.0 (669) | 37.7 (260) | 64 | |
| Rapid Trempe | 800 (427) | 95.0 (655) | 34.8 (240) | 65 | |
| 1000 (538) | 88.9 (613) | 33.8 (233) | 60 | ||
| Plak, 3/16 to 1.000" Epè |
Chalè trete nan | 400 (204) | 98.9 (682) | 38.2 (263) | 61 |
| 2050 degre F | 600 (316) | 94.3 (650) | 34.1 (235) | 66 | |
| Rapid Trempe | 800 (427) | 91.5 (631) | 32.7 (235) | 60 | |
| 1000 (538) | 87.2 (601) | 32.8 (226) | 59 | ||
| Plak, 1.000" Epè |
Chalè trete nan | Chanm | 113.9 (785) | 52.9 (365) | 59 |
| 2050 degre F | 600 (316) | 96.3 (664) | 36.2 (250) | 63 | |
| Rapid Trempe | 800 (427) | 94.8 (654) | 30.5 (210) | 61 |
Hastelloy C-276 (N10276) Pwopriyete Fizik:
- Dansite relatif 8.9g/cm3.
- Pwen k ap fonn 1025-17 degre.
Fèy Hastelloy C276Tretman Chalè
- Recuit:ASME SB 575 UNS N10276tanperati rkwit varye ant 1040 degre (1900 degre F) ak 1150 degre (2100 degre F) ki te swiv pa rapid trempe nan tanperati chanm.
- Solisyon Recuit: Solisyon Recuit ka fèt nan yon tanperati ki pi wo (apeprè 1175 degre (2150 degre F)) ki te swiv pa refwadisman rapid.
- Soulajman estrès: Lè2.4819 materyèlse soude oswa fòme, soulajman estrès nan alantou 760 degre (1400 degre F) ka diminye estrès rezidyèl ak amelyore estabilite nan dimansyon nan materyèl la.
D 'ASTM B575 Hastelloy C276
Akòz severite a ak travay redi tandans nan nikèl c276 plak, li nesesè yo chwazi zouti koupe apwopriye: zouti koupe carbure. Pwosesis la bezwen ralanti epi ajoute awozaj, elatriye.
ASTM B575 (C276) Hastelloy cho fòme
C-276 alyajse cho fòme imedyatman nan 1150 degre ak etenn ak dlo tiyo. Deformation frèt nan alyaj C276 ap ogmante fòs konpresiv li yo.
Founisè Pwosesis soude
Tankou gaz tengstèn arc soude (GTAW), gaz metal arc soude (GMAW), arc soude oswa lòt pwosesis soude.
FAQ
K: Konsènan pri fèy Hastelloy c276 pou chak kg?
K: Konbyen tan tan livrezon ou pran?
K: Èske gen sèvis echantiyon?
K: Ki kantite minimòm lòd?
K: Ki jan yo pake ASTM B575 N10276 pwodwi yo?
K: Peyi ekspòte yo
Baj popilè: hastelloy c276 fèy, hastelloy c276, 276 fèy, hastelloy fèy, din 2.4819
Pwochen
Fèy Hastelloy C2000Ou ka renmen tou
Voye rechèch